A facile solution-phase route for the preparation of AgInSe2 nanocrystals was developed by using silver nitrate, indium stearate, and oleylamine–selenium (OAm–Se) as precursors. The evolution process of the AgInSe2 nanocrystals is discussed in detail and different reaction conditions all have a great impact on the growth and morphology of the nanocrystals. Alloyed AgIn(S1−xSex)2nanocrystals with controlled composition across the entire range (0 ≤ x ≤ 1) was also successfully prepared by modulating the S/Se reactant mole ratio. X-ray diffraction (XRD), energy dispersive X-ray (EDX), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) were used to confirm that the alloyed AgIn(S1−xSex)2 nanocrystals are homogeneous. The UV-vis absorption spectra revealed that the band gap energies of the alloyed AgIn(S1−xSex)2 nanocrystals could be continuously tuned by increasing the Se content.
论文题目
A simple solution-phase approach to synthesize high quality ternary AgInSe2 and band gap tunable quaternary AgIn(S1−xSex)2 nanocrystals A simple solution-phase approach
发表刊物